1·George Ballas was born in Louisiana.

巴拉斯出生于路易斯安那州。

2·In all cases Raman spectra showed clearly the formation of the ballas diamond.

就一切情况而论，拉曼光谱明显反映了半刚石的形成。

3·Generally an increasing concentration in CHx compounds leads to ballas deposition.

通常情况是，chx化合物中浓度增大会导致半刚石沉积。

4·In flat ballas the D-band is smaller and the graphite peak larger than in coarse ballas.

在扁平的半刚石中，D带较小，而石墨峰比粗大的半刚石中的要大。

5·Ballas is a non-faceted, polycrystalline spherically grown diamond having a radial structure.

半刚石是一种具有径向结构的非多面、聚晶球状金刚石。

6·From the present point of view the ballas morphologies can be described by various microstructures.

按照目前的观点，半刚石的形貌可通过多种显微结构加以描述。

7·The ballas type grown at the transition to the graphitic deposition is characterized by a homogenous micro-twinned matrix.

在向石墨沉积转变中生成的半刚石种类的特征是均匀的显微孪晶基体。

8·Some examples should show that the deposition of faceted or ballas diamond is strongly related to the deposition parameters.

一些例子可以说明，多面金刚石或半刚石的沉积与沉积参数有着密切的关系。

9·Ballas types grown under conditions adjacent to the faceted diamond region were called coarse ballas in earlier publications.

在邻近多面金刚石区域的条件下生成的半刚石在以前的刊物中被称作粗大的半刚石。

10·In the present work the facts of ballas diamond deposition will be summarized and correlated with the described nano-crystalline diamond.

本文对半刚石沉积的实际情况进行了综述，并将它们与所述纳米晶金刚石联系起来。

半刚石

1·The described nano-crystalline diamond deposits show nearly the same Raman peaks as ballas deposits and also the TEM images look very similar.

上述纳米晶金刚石沉积物显示出与半刚石沉积物几乎相同的拉曼谱峰，而且TEM图象也十分相似。

2·The formation of ballas is observed with increasing carbon supersaturation (CH4 content) in the gas phase respectively with decreasing at. H/C ration.

随着H/C比率减小，气相中碳的超饱和度（CH4含量）相应增大，从而形成半刚石。

3·In general it is difficult to determine the exact transition temperature between ballas and faceted growth, due to numerous other parameters within an experimental setup.

总的来说，由于在一个实验装置内有许多其它参数，要准确测定半刚石和多面金刚石生长的转变温度是不容易的。

4·Generally an increasing concentration in CHx compounds leads to ballas deposition.

通常情况是，chx化合物中浓度增大会导致半刚石沉积。

5·Ballas is a non-faceted, polycrystalline spherically grown diamond having a radial structure.

半刚石是一种具有径向结构的非多面、聚晶球状金刚石。