全部

1·When webs weight increases, rupture strength, tearing strength and bursting strength are increased.

随着纤网定量的增加，断裂强度，撕破强度和顶破强度增加。

2·Results showed that sinter-HIP treatment can enhance the transverse rupture strength of WC-Co cemented carbides effectively.

结果表明：低压烧结工艺可以有效提高硬质合金的抗弯强度；

3·The hardness increased, but the density, transverse rupture strength and compressive strength decreased when prolonging the holding time.

随着球磨时间的延长，烧结合金的硬度升高，密度、横向断裂强度和压缩强度均下降。

4·The effects of milling time and sintering temperature on density, hardness, transverse rupture strength and compressive strength were mainly studied.

重点研究了球磨时间和烧结温度对烧结合金的密度、硬度、横向断裂强度和压缩强度的影响。

5·It was also found that at a fixed temperature the transverse-rupture strength of the alloy generally increased with the steepness of load-deflection curves.

还表明，在一定温度下，载荷-挠度曲线越陡，合金的抗弯强度一般也越高。

6·Transverse rupture strength, Rockwell a hardness, magnetic saturation induction and magnetic coercivity of samples sintered in vacuum or by sinter-HIP were measured.

测试了真空烧结和低压烧结试样的抗弯强度、洛氏硬度、磁饱和度和矫顽磁力。

7·The results showed that cemented carbide manufactured by sinter-HIP is free of porosity and transverse-rupture strength, bending fatigue life are also greatly increased.

结果表明，烧结-热等静压制作的硬质合金孔洞消除了，并且硬质合金的抗弯强度和弯曲疲劳寿命也大幅度提高。

8·The road performance test include: compression strength, cleavage strength, rupture strength, modulus of compression strength resilience, shrinkage, fatigue test and washout test.

路用性能的试验内容包括：抗压强度、劈裂强度、抗弯拉强度、抗压回弹模量、温缩干缩、抗冲刷试验、冻融试验和疲劳性能试验。

9·With good transversal rupture strength and wear resistance, it is suitable for low-speed rough turning and milling of heat resistanct alloys, titanium alloys and of plastics glass well.

具有很高的抗弯强度和良好的耐磨性能，适用与低速粗车和铣削耐热合金、 钛合金，也可加工玻璃钢。

10·Elevating sintering temperature, the density increased and the hardness decreased, but the transverse rupture strength and compressive strength were increased at first and then decreased.

随着烧结温度的升高，烧结合金的密度增加，硬度降低，横向断裂强度和压缩强度则先升高后降低。