1·The secondary recrystallization and its temperature range of grain oriented silicon steel have been studied by the method of interrupting secondary recrystallization annealing.

采用＂中断法＂研究了取向硅钢二次再结晶过程中的异常长大行为，确定了二次再结晶发生的温度范围。

2·The recrystallization textures after different annealing processes of 3104 aluminium alloy had been investigated by means of orientation distribution functions (ODFs).

应用取向分布函数(odf)研究和分析了3104铝合金经不同工艺退火后的再结晶织构。

3·In this paper, the copper sheets were subject to asymmetrical accumulative rolling-bonding (AARB) by different passes and recrystallization annealing.

本论文选用工业纯铜板材作为研究对象，对其进行了不同道次的异步叠轧和再结晶退火实验。

4·The experimental results showed that in the annealing condition the recrystallization texture has an important influence on the capacitance of etched al foil.

实验表明：在退火条件下，再结晶织构对腐蚀铝箔的电容量有重要影响。

5·The influence of trace Fe and annealing on recrystallization texture of high purity aluminum foils was investigated by means of orientation distribution functions(ODFs)and TEM.

采用晶体取向分布函数（O DF）、TEM研究了铁含量及退火对高纯铝箔再结晶织构的影响。

6·The different recrystallization annealing temperature and the micro-hardness of sample show the complex relationship.

不同的再结晶退火温度与试样的显微硬度表现出复杂关系。

7·But if the annealing temperature is too high these will appear coarse-grained structure resulting from entire recrystallization.

但是，如果温度过高，会因产生再结晶而出现粗晶组织，还会导致性能的严重恶化。

8·The microstructure and hardness of T2 copper subjected to stamping deformation at 77 K and subsequently recrystallization annealing were studied.

研究了工业纯铜T2在77 K温度下快速压缩变形的组织变化和再结晶退火温度、时间对其组织、性能的影响。

9·The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.

分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。

10·The annealing time should be long enough for complete recrystallization. Mechnical properties of the products produced in this way are excellent and stable.

工业生产和用户使用结果表明，产品冲压性能优良，质量稳定，完全满足用户的使用要求。