1·The antifouling properties of common materials have been studied with in-situ seawater immersion test.

通过海上挂片试验，研究了几种常用材料的防海生物污损性能。

2·The corrosion behavior of GECM coupled with the LY12CZ aluminum alloy was also observed in immersion test.

同时对偶接了LY 12 CZ铝合金的炭纤维环氧复合材料也进行了腐蚀浸泡对比试验。

3·The data of salt solution immersion test indicate that corrosion rate of aluminium alloy LY12 with ceria thin film is decreased.

盐水浸渍法试验结果证明了成膜后LY12铝合金表面的腐蚀速率明显降低；

4·The change of martensite content of AISI304 stainless steels in corrosion solution was also studied by means of immersion test and metalloscope.

通过浸泡试验和金相显微镜研究了30 4不锈钢在腐蚀过程中马氏体含量的变化。

5·For immersion tests and the polarization curve of the experimental test, nano-composite coating can increase the magnesium alloy corrosion resistance.

对纳米复合镀层进行浸泡试验和极化曲线的测定，表明纳米复合镀层能很好地提高镁合金的耐腐蚀性能。

6·Results of brine immersion test, co_2-saturated brine immersion test, salt spary test and so on showed that TY oil has good multiple antirust performance.

利用诸性能评定试验初步评定了该油品的防锈性能，结果表明TY防锈油具有较好的综合防锈性能。

7·The anticorrosive property of the conversion film was examined intensively by moisture and heating test, salt solution immersion test and electrochemical method.

利用湿热试验、盐水浸渍试验及电化学测试方法评价了膜的耐蚀性能。

8·To systematically study the effects of mineral admixtures such as slag, expanding agent on sulfate resistance of concrete, a series of concrete immersion test was carried out.

通过混凝土的抗硫酸盐浸泡试验，系统研究了矿渣、膨胀剂等矿物掺合料对混凝土抗硫酸盐侵蚀性能的影响。

9·The influence of the test methods to the estimation of the water stability of asphalt mixtures was researched by comparing the general immersion tests, the immersion rutting test and the HWTD.

通过对沥青混合料常规水稳试验、浸水车辙试验及汉堡车辙试验（HWTD）的比较，分析了不同试验方法对沥青混合料水稳定性评价的影响。

10·Optical fibres - Part 1-53: measurement methods and test procedures - Water immersion.

光学纤维。第1 - 53部分：测量方法和试验程序。水浸渍。