1·A flexible epoxy acrylate resin prepolymer was prepared.

制得柔性环氧丙烯酸酯预聚体。

2·Epoxy acrylate was synthesised by reacting epoxy resin with acrylic acid.

用丙烯酸和环氧树脂合成了丙烯酸环氧酯。

3·The synthesis of epoxy acrylate type photosensitive coatings were developed by semi-ester method.

开发了一种用半酯法合成环氧丙烯酸酯型光敏涂料的方法。

4·The epoxy acrylate was synthesized with different amounts of inhibitor, feed ratios and feeding modes.

在不同阻聚剂用量、投料比、投料方式等条件下合成环氧丙烯酸酯。

5·The hydroxyl groups of epoxy acrylate (AAEP) in VER were sealed with different methods in order to obtain modified VER.

采用不同的方法对乙烯基酯树脂(ver)中环氧丙烯酸酯(AAEP)进行羟基封闭，制备改性ver。

6·Through vulcanization curves evaluation ammonium benzoate was selected as the vulcanizing agent of epoxy acrylate rubber (EACM).

通过硫化曲线评定，选用苯甲酸铵作硫化剂对环氧型丙烯酸酯橡胶低温胶进行硫化。

7·Epoxy acrylate (EA) resin is an important photosensitive resin, in which bisphenolic epoxide was most widely used in the field of UV curing coating.

环氧丙烯酸（ EA） 树脂在辐射固化领域中是一种重要的感光树脂，其中双酚A型环氧树脂的应用最为广泛。

8·The invention belongs to the field of synthesizing organic chemical materials and discloses modified bisphenol a epoxy acrylate and a preparation method thereof.

本发明属于有机化学材料合成领域，公开了一种改性双酚a环氧丙烯酸酯及其制备方法。

9·The title UV curing coatings is prepared based on epoxy acrylate, reactive diluents and photoinitiator. The main raw materials and cured film are tested with TGA.

以环氧丙烯酸酯、活性稀释单体、光引发剂等为原料，制备UV固化涂层，对主要原料及固化后的涂层进行了热失质量分析。

10·It was showed from the experiment that: epoxy acrylate oligomers had good adhesiveness and dye wettability, high luster and rigidity, and excellent solvent resistance;

通过实验可以看出：环氧丙烯酸酯齐聚物具有良好的附着力、颜料润湿性、高光泽、高硬度与优异的耐溶解性；